Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions
The aim of this work is to investigate which alloying element in C-22 is responsible for the cracking susceptibility of the alloy in bicarbonate and two buffer solutions (tungstate and borate). Six nickel based alloys, with different amount of chromium (Cr) and molybdenum (Mo) were tested using elec...
Guardado en:
Autores principales: | , , , , |
---|---|
Formato: | JOUR |
Materias: | |
Acceso en línea: | http://hdl.handle.net/20.500.12110/paper_0010938X_v108_n_p1_Zadorozne |
Aporte de: |
id |
todo:paper_0010938X_v108_n_p1_Zadorozne |
---|---|
record_format |
dspace |
spelling |
todo:paper_0010938X_v108_n_p1_Zadorozne2023-10-03T14:09:32Z Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions Zadorozne, N.S. Giordano, M.C. Ares, A.E. Carranza, R.M. Rebak, R.B. Nickel Polarization Stress corrosion Alloying elements Corrosion Cracks Molybdenum Nickel Polarization Residual stresses Strain rate Anodic potentials Buffer solutions Cracking susceptibility ELectrochemical methods Nickel based alloy Slow strain rate tests Stress corrosion Transgranular cracking Stress corrosion cracking The aim of this work is to investigate which alloying element in C-22 is responsible for the cracking susceptibility of the alloy in bicarbonate and two buffer solutions (tungstate and borate). Six nickel based alloys, with different amount of chromium (Cr) and molybdenum (Mo) were tested using electrochemical methods and slow strain rate tests (SSRT) at 90 °C. All Cr containing alloys had transgranular cracking at high anodic potential; however, C-22 containing high Cr and high Mo was the most susceptible alloy to cracking. Bicarbonate was the most aggressive of three tested environments of similar pH. © 2016 Elsevier Ltd. Fil:Carranza, R.M. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales; Argentina. JOUR info:eu-repo/semantics/openAccess http://creativecommons.org/licenses/by/2.5/ar http://hdl.handle.net/20.500.12110/paper_0010938X_v108_n_p1_Zadorozne |
institution |
Universidad de Buenos Aires |
institution_str |
I-28 |
repository_str |
R-134 |
collection |
Biblioteca Digital - Facultad de Ciencias Exactas y Naturales (UBA) |
topic |
Nickel Polarization Stress corrosion Alloying elements Corrosion Cracks Molybdenum Nickel Polarization Residual stresses Strain rate Anodic potentials Buffer solutions Cracking susceptibility ELectrochemical methods Nickel based alloy Slow strain rate tests Stress corrosion Transgranular cracking Stress corrosion cracking |
spellingShingle |
Nickel Polarization Stress corrosion Alloying elements Corrosion Cracks Molybdenum Nickel Polarization Residual stresses Strain rate Anodic potentials Buffer solutions Cracking susceptibility ELectrochemical methods Nickel based alloy Slow strain rate tests Stress corrosion Transgranular cracking Stress corrosion cracking Zadorozne, N.S. Giordano, M.C. Ares, A.E. Carranza, R.M. Rebak, R.B. Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions |
topic_facet |
Nickel Polarization Stress corrosion Alloying elements Corrosion Cracks Molybdenum Nickel Polarization Residual stresses Strain rate Anodic potentials Buffer solutions Cracking susceptibility ELectrochemical methods Nickel based alloy Slow strain rate tests Stress corrosion Transgranular cracking Stress corrosion cracking |
description |
The aim of this work is to investigate which alloying element in C-22 is responsible for the cracking susceptibility of the alloy in bicarbonate and two buffer solutions (tungstate and borate). Six nickel based alloys, with different amount of chromium (Cr) and molybdenum (Mo) were tested using electrochemical methods and slow strain rate tests (SSRT) at 90 °C. All Cr containing alloys had transgranular cracking at high anodic potential; however, C-22 containing high Cr and high Mo was the most susceptible alloy to cracking. Bicarbonate was the most aggressive of three tested environments of similar pH. © 2016 Elsevier Ltd. |
format |
JOUR |
author |
Zadorozne, N.S. Giordano, M.C. Ares, A.E. Carranza, R.M. Rebak, R.B. |
author_facet |
Zadorozne, N.S. Giordano, M.C. Ares, A.E. Carranza, R.M. Rebak, R.B. |
author_sort |
Zadorozne, N.S. |
title |
Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions |
title_short |
Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions |
title_full |
Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions |
title_fullStr |
Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions |
title_full_unstemmed |
Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions |
title_sort |
anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions |
url |
http://hdl.handle.net/20.500.12110/paper_0010938X_v108_n_p1_Zadorozne |
work_keys_str_mv |
AT zadoroznens anodiccharacteristicsandstresscorrosioncrackingbehaviorofnickelrichalloysinbicarbonateandbuffersolutions AT giordanomc anodiccharacteristicsandstresscorrosioncrackingbehaviorofnickelrichalloysinbicarbonateandbuffersolutions AT aresae anodiccharacteristicsandstresscorrosioncrackingbehaviorofnickelrichalloysinbicarbonateandbuffersolutions AT carranzarm anodiccharacteristicsandstresscorrosioncrackingbehaviorofnickelrichalloysinbicarbonateandbuffersolutions AT rebakrb anodiccharacteristicsandstresscorrosioncrackingbehaviorofnickelrichalloysinbicarbonateandbuffersolutions |
_version_ |
1782025677150617600 |