Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line
A post mortem MgO-C brick of a steel ladle (slag line) was studied to identify the main causes of a localized wear, produced at initial taps. The extreme low thickness of the lining provokes ladle removed from service. In addition, slag infiltration into the upper horizontal joint promotes corrosion...
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | Documento de conferencia publisherVersion |
| Lenguaje: | Inglés |
| Publicado: |
Research Waves Ltd.
2022
|
| Materias: | |
| Acceso en línea: | https://materialssummit.researchwaves.com/ http://hdl.handle.net/20.500.12272/7420 |
| Aporte de: |
| id |
I68-R174-20.500.12272-7420 |
|---|---|
| record_format |
dspace |
| institution |
Universidad Tecnológica Nacional |
| institution_str |
I-68 |
| repository_str |
R-174 |
| collection |
RIA - Repositorio Institucional Abierto (UTN) |
| language |
Inglés |
| topic |
wear microstructure refractories thermodynamic simulation |
| spellingShingle |
wear microstructure refractories thermodynamic simulation Brandaleze, Elena Benavidez, Edgardo Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line |
| topic_facet |
wear microstructure refractories thermodynamic simulation |
| description |
A post mortem MgO-C brick of a steel ladle (slag line) was studied to identify the main causes of a localized wear, produced at initial taps. The extreme low thickness of the lining provokes ladle removed from service. In addition, slag infiltration into the upper horizontal joint promotes corrosion. The slag line presents cracks with a propagation pattern considerably parallel to the hot face. In order to identify the wear mechanisms, the results of the postmorten study were compared with information of the characterization of one brick without use. |
| format |
Documento de conferencia publisherVersion |
| author |
Brandaleze, Elena Benavidez, Edgardo |
| author_facet |
Brandaleze, Elena Benavidez, Edgardo |
| author_sort |
Brandaleze, Elena |
| title |
Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line |
| title_short |
Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line |
| title_full |
Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line |
| title_fullStr |
Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line |
| title_full_unstemmed |
Failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line |
| title_sort |
failure caused by multiple mechanisms that produce a premature localized wear of a steel ladle slag line |
| publisher |
Research Waves Ltd. |
| publishDate |
2022 |
| url |
https://materialssummit.researchwaves.com/ http://hdl.handle.net/20.500.12272/7420 |
| work_keys_str_mv |
AT brandalezeelena failurecausedbymultiplemechanismsthatproduceaprematurelocalizedwearofasteelladleslagline AT benavidezedgardo failurecausedbymultiplemechanismsthatproduceaprematurelocalizedwearofasteelladleslagline |
| bdutipo_str |
Repositorios |
| _version_ |
1764820552607858688 |