Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS)

Mostrar todas las versiones(3)

The metallic coating of zinc alloyed with other metals such as nickel, has very good corrosion resistance. It was found that the type and quantity of particles, increases the hardness and the nickel content in the alloy at all current densities. Photomicrographs were made in electronic and optical m...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Mahmud, Z., Amelotti, F., Lloret, P., Gagliardi, J., Túlio, P., Míngolo, N., Gassa, L., Gordillo, G.
Formato: Informe técnico submittedVersion
Lenguaje:Español
Publicado: Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales 2016
Materias:
Zn Ni alloys,
electro deposition
ceramic particles
structural characterization
corrosion resistance
microhardness
Acceso en línea:http://hdl.handle.net/20.500.12110/technicalreport_n00011
http://repositoriouba.sisbi.uba.ar/gsdl/cgi-bin/library.cgi?a=d&c=aexreport&d=technicalreport_n00011_oai
Aporte de:
Repositorio Digital de la Universidad de Buenos Aires (UBA) de Universidad de Buenos Aires
id I28-R145-technicalreport_n00011_oai
record_format dspace
spelling I28-R145-technicalreport_n00011_oai2020-04-23 Mahmud, Z. Amelotti, F. Lloret, P. Gagliardi, J. Túlio, P. Míngolo, N. Gassa, L. Gordillo, G. 2016-07 The metallic coating of zinc alloyed with other metals such as nickel, has very good corrosion resistance. It was found that the type and quantity of particles, increases the hardness and the nickel content in the alloy at all current densities. Photomicrographs were made in electronic and optical microscope (in samples with particle, cross sectional views). We have found that there is an optimum thickness of 10 microns in which the intensity of texture in the material is increased. In this thickness in ZnNi - Al2O3, the Charge Transference Resistance, RTC in ohm, measured by Impedance was RTC ZnNi + Al2O3 > RTC ZnNi and in the Polarization Curves the corrosion current density is decreased. In salt spray tests on samples with the same thickness, it was found that the area with white rust is lower for Zn Ni with Al2O3 on the affected area that in other cases. Fil: Mahmud, Z. Instituto Nacional de Tecnología Industrial; Argentina. Fil: Amelotti, F. Instituto Nacional de Tecnología Industrial; Argentina. Fil: Lloret, P. Instituto Nacional de Tecnología Industrial; Argentina. Fil: Gagliardi, J. Instituto Nacional de Tecnología Industrial; Argentina. Fil: Túlio, P. Universidade Tecnológica Federal do Paraná; Brasil. Fil: Míngolo, N. Comisión Nacional de Energía Atómica; Argentina. Fil: Gassa, L. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina. Fil: Gordillo, G. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; Argentina. application/pdf http://hdl.handle.net/20.500.12110/technicalreport_n00011 spa Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales info:eu-repo/semantics/openAccess http://creativecommons.org/licenses/by/2.5/ar Zn Ni alloys, electro deposition ceramic particles structural characterization corrosion resistance microhardness Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS) info:eu-repo/semantics/report info:ar-repo/semantics/informe técnico info:eu-repo/semantics/submittedVersion http://repositoriouba.sisbi.uba.ar/gsdl/cgi-bin/library.cgi?a=d&c=aexreport&d=technicalreport_n00011_oai
institution Universidad de Buenos Aires
institution_str I-28
repository_str R-145
collection Repositorio Digital de la Universidad de Buenos Aires (UBA)
language Español
orig_language_str_mv spa
topic Zn Ni alloys,
electro deposition
ceramic particles
structural characterization
corrosion resistance
microhardness
spellingShingle Zn Ni alloys,
electro deposition
ceramic particles
structural characterization
corrosion resistance
microhardness
Mahmud, Z.
Amelotti, F.
Lloret, P.
Gagliardi, J.
Túlio, P.
Míngolo, N.
Gassa, L.
Gordillo, G.
Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS)
topic_facet Zn Ni alloys,
electro deposition
ceramic particles
structural characterization
corrosion resistance
microhardness
description The metallic coating of zinc alloyed with other metals such as nickel, has very good corrosion resistance. It was found that the type and quantity of particles, increases the hardness and the nickel content in the alloy at all current densities. Photomicrographs were made in electronic and optical microscope (in samples with particle, cross sectional views). We have found that there is an optimum thickness of 10 microns in which the intensity of texture in the material is increased. In this thickness in ZnNi - Al2O3, the Charge Transference Resistance, RTC in ohm, measured by Impedance was RTC ZnNi + Al2O3 > RTC ZnNi and in the Polarization Curves the corrosion current density is decreased. In salt spray tests on samples with the same thickness, it was found that the area with white rust is lower for Zn Ni with Al2O3 on the affected area that in other cases.
format Informe técnico
Informe técnico
submittedVersion
author Mahmud, Z.
Amelotti, F.
Lloret, P.
Gagliardi, J.
Túlio, P.
Míngolo, N.
Gassa, L.
Gordillo, G.
author_facet Mahmud, Z.
Amelotti, F.
Lloret, P.
Gagliardi, J.
Túlio, P.
Míngolo, N.
Gassa, L.
Gordillo, G.
author_sort Mahmud, Z.
title Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS)
title_short Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS)
title_full Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS)
title_fullStr Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS)
title_full_unstemmed Intensidad de texturas vs espesores en Aleaciones de Zinc-Níquel + Micropartículas de Alúmina. Caracterización del material (Dureza, Contenido de Níquel %, XRD, AFM, SEM, FRX, EIS)
title_sort intensidad de texturas vs espesores en aleaciones de zinc-níquel + micropartículas de alúmina. caracterización del material (dureza, contenido de níquel %, xrd, afm, sem, frx, eis)
publisher Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales
publishDate 2016
url http://hdl.handle.net/20.500.12110/technicalreport_n00011
http://repositoriouba.sisbi.uba.ar/gsdl/cgi-bin/library.cgi?a=d&c=aexreport&d=technicalreport_n00011_oai
work_keys_str_mv AT mahmudz intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
AT amelottif intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
AT lloretp intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
AT gagliardij intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
AT tuliop intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
AT mingolon intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
AT gassal intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
AT gordillog intensidaddetexturasvsespesoresenaleacionesdezincniquelmicroparticulasdealuminacaracterizaciondelmaterialdurezacontenidodeniquelxrdafmsemfrxeis
_version_ 1766017950687428608

Ejemplares similares