Behavior of Electrogalvanized Steel Pre-Treated with Cr(III)-Based Baths and Exposed to 0.5 M Na<SUB>2</SUB>SO<SUB>4</SUB> Solution
As Cr (VI) compounds used to formulate conversion layers provide enhanced anticorrosive protection to zinc coatings, but they are produced using hazardous chemicals, the development of “green” technologies is a paramount purpose. Consequently, the corrosion behavior of zinc coatings subjected to a C...
Guardado en:
Autores principales: | , , |
---|---|
Formato: | Articulo |
Lenguaje: | Inglés |
Publicado: |
2012
|
Materias: | |
Acceso en línea: | http://sedici.unlp.edu.ar/handle/10915/82168 http://www.scielo.mec.pt/pdf/pea/v30n3/v30n3a01.pdf |
Aporte de: |
id |
I19-R120-10915-82168 |
---|---|
record_format |
dspace |
institution |
Universidad Nacional de La Plata |
institution_str |
I-19 |
repository_str |
R-120 |
collection |
SEDICI (UNLP) |
language |
Inglés |
topic |
Ingeniería Química Corrosion Trivalent chromium Conversion layer Sealing treatment Electrogalvanized steel |
spellingShingle |
Ingeniería Química Corrosion Trivalent chromium Conversion layer Sealing treatment Electrogalvanized steel Tomachuk, C. R. Elsner, Cecilia Inés Di Sarli, Alejandro Ramón Behavior of Electrogalvanized Steel Pre-Treated with Cr(III)-Based Baths and Exposed to 0.5 M Na<SUB>2</SUB>SO<SUB>4</SUB> Solution |
topic_facet |
Ingeniería Química Corrosion Trivalent chromium Conversion layer Sealing treatment Electrogalvanized steel |
description |
As Cr (VI) compounds used to formulate conversion layers provide enhanced anticorrosive protection to zinc coatings, but they are produced using hazardous chemicals, the development of “green” technologies is a paramount purpose. Consequently, the corrosion behavior of zinc coatings subjected to a Cr3+ based passivating treatment, with and without sealing, was studied through EIS measurements in 0.5 M Na2SO4 solution. The analyses of the experimental data allowed inferring that the Cr3+-based conversion treatment with an adequate sealer provides good corrosion resistance and, coupled to an adequate painting system, could be a suitable alternative to traditional chromate coatings. |
format |
Articulo Articulo |
author |
Tomachuk, C. R. Elsner, Cecilia Inés Di Sarli, Alejandro Ramón |
author_facet |
Tomachuk, C. R. Elsner, Cecilia Inés Di Sarli, Alejandro Ramón |
author_sort |
Tomachuk, C. R. |
title |
Behavior of Electrogalvanized Steel Pre-Treated with Cr(III)-Based Baths and Exposed to 0.5 M Na<SUB>2</SUB>SO<SUB>4</SUB> Solution |
title_short |
Behavior of Electrogalvanized Steel Pre-Treated with Cr(III)-Based Baths and Exposed to 0.5 M Na<SUB>2</SUB>SO<SUB>4</SUB> Solution |
title_full |
Behavior of Electrogalvanized Steel Pre-Treated with Cr(III)-Based Baths and Exposed to 0.5 M Na<SUB>2</SUB>SO<SUB>4</SUB> Solution |
title_fullStr |
Behavior of Electrogalvanized Steel Pre-Treated with Cr(III)-Based Baths and Exposed to 0.5 M Na<SUB>2</SUB>SO<SUB>4</SUB> Solution |
title_full_unstemmed |
Behavior of Electrogalvanized Steel Pre-Treated with Cr(III)-Based Baths and Exposed to 0.5 M Na<SUB>2</SUB>SO<SUB>4</SUB> Solution |
title_sort |
behavior of electrogalvanized steel pre-treated with cr(iii)-based baths and exposed to 0.5 m na<sub>2</sub>so<sub>4</sub> solution |
publishDate |
2012 |
url |
http://sedici.unlp.edu.ar/handle/10915/82168 http://www.scielo.mec.pt/pdf/pea/v30n3/v30n3a01.pdf |
work_keys_str_mv |
AT tomachukcr behaviorofelectrogalvanizedsteelpretreatedwithcriiibasedbathsandexposedto05mnasub2subsosub4subsolution AT elsnerceciliaines behaviorofelectrogalvanizedsteelpretreatedwithcriiibasedbathsandexposedto05mnasub2subsosub4subsolution AT disarlialejandroramon behaviorofelectrogalvanizedsteelpretreatedwithcriiibasedbathsandexposedto05mnasub2subsosub4subsolution |
bdutipo_str |
Repositorios |
_version_ |
1764820487925399554 |