Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D₅₀ 0.8 µm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed micros...
Guardado en:
Autores principales: | , , , , |
---|---|
Formato: | Articulo |
Lenguaje: | Inglés |
Publicado: |
2018
|
Materias: | |
Acceso en línea: | http://sedici.unlp.edu.ar/handle/10915/128588 |
Aporte de: |
id |
I19-R120-10915-128588 |
---|---|
record_format |
dspace |
institution |
Universidad Nacional de La Plata |
institution_str |
I-19 |
repository_str |
R-120 |
collection |
SEDICI (UNLP) |
language |
Inglés |
topic |
Ciencias Exactas Química Zircon Processing Milling Sintering XRD-Rietveld |
spellingShingle |
Ciencias Exactas Química Zircon Processing Milling Sintering XRD-Rietveld Gauna, Matías Roberto Conconi, María Susana Suárez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route |
topic_facet |
Ciencias Exactas Química Zircon Processing Milling Sintering XRD-Rietveld |
description |
In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D₅₀ 0.8 µm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa. |
format |
Articulo Articulo |
author |
Gauna, Matías Roberto Conconi, María Susana Suárez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author_facet |
Gauna, Matías Roberto Conconi, María Susana Suárez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author_sort |
Gauna, Matías Roberto |
title |
Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route |
title_short |
Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route |
title_full |
Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route |
title_fullStr |
Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route |
title_full_unstemmed |
Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route |
title_sort |
dense zircon (zrsio<sub>4</sub>) ceramics by a simple milling-sintering route |
publishDate |
2018 |
url |
http://sedici.unlp.edu.ar/handle/10915/128588 |
work_keys_str_mv |
AT gaunamatiasroberto densezirconzrsiosub4subceramicsbyasimplemillingsinteringroute AT conconimariasusana densezirconzrsiosub4subceramicsbyasimplemillingsinteringroute AT suarezgustavo densezirconzrsiosub4subceramicsbyasimplemillingsinteringroute AT agliettiestebanfausto densezirconzrsiosub4subceramicsbyasimplemillingsinteringroute AT rendtorffbirrernicolasmaximiliano densezirconzrsiosub4subceramicsbyasimplemillingsinteringroute |
bdutipo_str |
Repositorios |
_version_ |
1764820452570562561 |