Effect of Cr III passivation on the corrosion resistance of coated electrogalvanized steel

Electrogalvanized steel surfaces are usually passivated for corrosion protection. Many of the passivation processes involve the use of hexavalent chromium (yellow chromating) that is being increasingly banished due to its toxic and carcinogenic effects. The search of alternative treatments for repla...

Descripción completa

Detalles Bibliográficos
Autores principales: Queiroz, F. M., Elsner, Cecilia Inés, Di Sarli, Alejandro Ramón, Tomachuk, C., Costa, I.
Formato: Objeto de conferencia Resumen
Lenguaje:Inglés
Publicado: 2011
Materias:
Química
Acero
Corrosión
Protección
Acceso en línea:http://sedici.unlp.edu.ar/handle/10915/119315
Aporte de:
SEDICI (UNLP) de Universidad Nacional de La Plata
id I19-R120-10915-119315
record_format dspace
institution Universidad Nacional de La Plata
institution_str I-19
repository_str R-120
collection SEDICI (UNLP)
language Inglés
topic Química
Acero
Corrosión
Protección
spellingShingle Química
Acero
Corrosión
Protección
Queiroz, F. M.
Elsner, Cecilia Inés
Di Sarli, Alejandro Ramón
Tomachuk, C.
Costa, I.
Effect of Cr III passivation on the corrosion resistance of coated electrogalvanized steel
topic_facet Química
Acero
Corrosión
Protección
description Electrogalvanized steel surfaces are usually passivated for corrosion protection. Many of the passivation processes involve the use of hexavalent chromium (yellow chromating) that is being increasingly banished due to its toxic and carcinogenic effects. The search of alternative treatments for replacement of the yellow chromating has been the aim of many research carried out in the last decades. Among the proposed surface treatments, those based on Cr III solutions have been related to the highest compatibility to the Cr VI based ones. The present study evaluates the corrosion resistance of electrogalvanized steel passivated in Cr III or Cr VI based solutions and compares the effects of these two types of passivation treatments for samples with organic coating on top of the passivating surface film. Galvanizing of steel samples was carried out in an alkaline cyanide free zinc solution. Next, the electrogalvanized steel samples were passivated, either in a Cr III or a Cr VI based solutions, and then covered with an organic coating formulated specifically for this investigation. The electrochemical behavior of the prepared samples was monitored as a function of immersion time by electrochemical impedance spectroscopy (EIS) in a 0.05 mol L-1 sodium chloride solution, as Figure 1 illustrates. The results show that although higher impedances were associated to the Cr VI based treatments along the test period (4 days), it largely decreased between the first hours and 1 day of immersion, and remained fairly stable for longer periods. For the Cr III passivated samples, however, the impedance continuously increased with time of immersion, due to sealing of the defects in the passive film with zinc products.
format Objeto de conferencia
Resumen
author Queiroz, F. M.
Elsner, Cecilia Inés
Di Sarli, Alejandro Ramón
Tomachuk, C.
Costa, I.
author_facet Queiroz, F. M.
Elsner, Cecilia Inés
Di Sarli, Alejandro Ramón
Tomachuk, C.
Costa, I.
author_sort Queiroz, F. M.
title Effect of Cr III passivation on the corrosion resistance of coated electrogalvanized steel
title_short Effect of Cr III passivation on the corrosion resistance of coated electrogalvanized steel
title_full Effect of Cr III passivation on the corrosion resistance of coated electrogalvanized steel
title_fullStr Effect of Cr III passivation on the corrosion resistance of coated electrogalvanized steel
title_full_unstemmed Effect of Cr III passivation on the corrosion resistance of coated electrogalvanized steel
title_sort effect of cr iii passivation on the corrosion resistance of coated electrogalvanized steel
publishDate 2011
url http://sedici.unlp.edu.ar/handle/10915/119315
work_keys_str_mv AT queirozfm effectofcriiipassivationonthecorrosionresistanceofcoatedelectrogalvanizedsteel
AT elsnerceciliaines effectofcriiipassivationonthecorrosionresistanceofcoatedelectrogalvanizedsteel
AT disarlialejandroramon effectofcriiipassivationonthecorrosionresistanceofcoatedelectrogalvanizedsteel
AT tomachukc effectofcriiipassivationonthecorrosionresistanceofcoatedelectrogalvanizedsteel
AT costai effectofcriiipassivationonthecorrosionresistanceofcoatedelectrogalvanizedsteel
bdutipo_str Repositorios
_version_ 1764820448180174849

Ejemplares similares