Photocatalytic activity of TiO2 thin films deposited by cathodic arc

Mostrar otras versiones (2)

In this work, the photocatalytic activity and the kinetic behavior of anatase TiO2 films deposited by cathodic arc (CA films) on glass substrates are reported and compared with those of TiO2 Degussa P-25 films obtained by dip-coating immersion (DC films). The mass density of films, determined by X-r...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autor principal: Kleiman, Ariel Javier
Otros Autores: Márquez, Adriana Beatriz, Vera, M.L, Meichtry, J.M, Litter, M.I
Formato: Capítulo de libro
Lenguaje:Inglés
Publicado: 2011
Acceso en línea:Registro en Scopus
DOI
Handle
Registro en la Biblioteca Digital
Aporte de:Registro referencial: Solicitar el recurso aquí
Biblioteca Central Dr. Luis F. Leloir (FCEN) de Universidad de Buenos Aires
LEADER 09428caa a22012257a 4500
001 PAPER-10862
003 AR-BaUEN
005 20250805131955.0
008 190411s2011 xx ||||fo|||| 00| 0 eng|d
024 7 |2 scopus  |a 2-s2.0-78650306520 
030 |a ACBEE 
040 |a Scopus  |b spa  |c AR-BaUEN  |d AR-BaUEN 
100 1 |a Kleiman, Ariel Javier 
245 1 0 |a Photocatalytic activity of TiO2 thin films deposited by cathodic arc 
260 |c 2011 
270 1 0 |m Márquez, A.; Instituto de Física del Plasma, Conicet, fcen, Universidad de Buenos Aires, Ciudad Universitaria Pab. I, 1428 Buenos Aires, Argentina; email: amarquez@df.uba.ar 
504 |a Kitano, M., Matsuoka, M., Ueshima, M., Anpo, M., (2007) Appl. Catal. A, 325, pp. 1-14 
504 |a Litter, M.I., (1999) Appl. Catal. B, 23, pp. 89-114 
504 |a Dijkstra, M.F.J., Buwalda, H., de Jong, A.W.F., Michorius, A., Winkelman, J.G.M., Beenackers, A.A.C.M., (2001) Chem. Eng. Sci., 56, pp. 547-555 
504 |a Hurum, D.C., Agrios, A.G., Gray, K.A., Rajh, T., Thurnauer, M.C., (2003) J. Phys. Chem. B, 107, pp. 4545-4549 
504 |a Sun, L., An, T., Wan, S., Li, G., Bao, N., Hu, X., Fu, J., Sheng, G., (2009) Sep. Purif. Technol., 68, pp. 83-89 
504 |a Brinker, C.J., Hurd, A.J., (1994) J. Phys. III (France), 4, pp. 1231-1242 
504 |a Piperata, G., Meichtry, J.M., Litter, M.I., (2004) Prog. Colloid Polym. Sci., 128, pp. 303-308 
504 |a Meichtry, J.M., Lin, H.J., de la Fuente, L., Levy, I.K., Gautier, E.A., Blesa, M.A., Litter, M.I., (2007) J. Solar Energy Eng., 129, pp. 119-126 
504 |a Brunella, M.F., Diamanti, M.V., Pedeferri, M.P., Fonzo, F.D., Casari, C.S., Bassi, A.L., (2007) Thin Solid Films, 515, pp. 6309-6313 
504 |a Hatanaka, Y., Naito, H., Itou, S., Kando, M., (2005) Appl. Surf. Sci., 244, pp. 554-557 
504 |a Zywitzki, O., Modes, T., Sahm, H., Frach, P., Goedicke, K., Glöß, D., (2004) Surf. Coat. Technol., pp. 538-543 
504 |a Kleiman, A., Márquez, A., Lamas, D.G., (2007) Surf. Coat. Technol., 201, pp. 6358-6362 
504 |a Vera, M.L., (2008), Preparación de fotocatalizadores de TiO2 soportados para su uso en potabilización de aguas, Master Thesis, Instituto de Tecnología Prof. Jorge A. Sabato, Universidad Nacional de General San Martín, Buenos Aires; Navío, J.A., Testa, J.J., Djedjeian, P., Padrón, J.R., Rodríguez, D., Litter, M.I., (1999) Appl. Catal. A, 178, pp. 191-203 
504 |a Testa, J.J., Grela, M.A., Litter, M.I., (2001) Langmuir, 17, pp. 3515-3517 
504 |a (2006) Guidelines for Drinking-water Quality, 3rd ed., Incorporating 1st and 2nd Addenda. Vol. 1, Recommendations, , World Health Organization 
504 |a Márquez, A., Blanco, G., Fernandez de Rapp, M.E., Lamas, D.G., Tarulla, R., (2004) Surf. Coat. Technol., 187, pp. 154-160 
504 |a Lin, W.-Y., Wei, C., Rajeshwar, K., (1993) J. Electrochem. Soc., 140, pp. 2477-2482 
504 |a Parrat, L.G., (1954) Phys. Rev., 95, pp. 359-369 
504 |a Henke, B.L., Gullikson, E.M., Davis, J.C., (1993) At. Data Nucl. Data Tables, 54, pp. 181-342 
504 |a Kuzmany, H., (1998) Solid-State Spectroscopy: An Introduction, , Springer-Verlag, Berlin 
504 |a Tauc, J., (1970) Mater. Res. Bull., 5, pp. 721-729 
504 |a Takikawa, H., Matsui, T., Sakakibara, T., Bendavid, A., Martin, P.J., (1999) Thin Solid Films, 348, pp. 145-151 
504 |a Bickley, R.I., Gonzalez-Carreno, T., Lees, J.S., Palmisano, L., Tilley, R.J.D., (1991) J. Solid State Chem., 92, pp. 178-190 
504 |a Martin, S.T., Herrmann, H., Hoffmann, M.R., (1994) J. Chem. Soc. Faraday Trans., 90, pp. 3323-3330 
504 |a Chong, M.N., Jin, B., Chow, C.W.K., Saint, C., (2010) Water Res., 44, pp. 2997-3027 
504 |a Emilio, C.A., Testa, J.J., Hufschmidt, D., Colón, G., Navío, J.A., Bahnemann, D.W., Litter, M.I., (2004) J. Ind. Eng. Chem., 10, pp. 129-138 
504 |a Mytych, P., Ciesla, P., Stasicka, Z., (2005) Appl. Catal. B, 59, pp. 161-170 
504 |a Ciesla, P., Kocot, P., Mytych, P., Stasicka, Z., (2004) J. Mol. Catal. A, 224, pp. 17-33 
504 |a Prairie, M.R., Evans, L.R., Stange, B., Martínez, S.L., (1993) Environ. Sci. Technol., 27, pp. 1776-1782 
504 |a Wang, L., Wang, N., Zhu, L., Yu, H., Tang, H., (2008) J. Hazard. Mater., 152, pp. 93-99 
504 |a Cappelletti, G., Bianchi, C.L., Ardizzone, S., (2008) Appl. Catal. B, 78, pp. 193-201 
504 |a Hongxiang, F., Gongxuan, L., Shuben, L., (1998) Adsorpt. Sci. Technol., 16, pp. 117-126 
504 |a Camera-Roda, G., Santarelli, F., (2007) Catal. Today, 129, pp. 161-168 
506 |2 openaire  |e Política editorial 
520 3 |a In this work, the photocatalytic activity and the kinetic behavior of anatase TiO2 films deposited by cathodic arc (CA films) on glass substrates are reported and compared with those of TiO2 Degussa P-25 films obtained by dip-coating immersion (DC films). The mass density of films, determined by X-ray reflectometry was 20% lower for DC films compared with CA films, indicating a higher porosity of DC samples. The activity was evaluated from the efficiency to reduce Cr(VI) in the presence of EDTA. Although the response of CA films resulted lower compared with that of P-25 films of the same TiO2 content (e.g. 90% vs. 50% Cr(VI) reduction after 180min irradiation for samples with 0.03mgcm-2 of TiO2), a fact associated to the lower porosity, adhesion properties of the new materials were much better. CA film photoactivity improved by increasing the coating thickness; after 180min, a sample with 0.03mgcm-2 of TiO2 presented 50% of Cr(VI) reduction vs. 80% for a sample with 0.28mgcm-2. These photocatalysts, whose preparation is simple and affordable, are very promising to be used as immobilized materials in photoreactors for the treatment of pollutants in gaseous and aqueous systems. © 2010 Elsevier B.V.  |l eng 
536 |a Detalles de la financiación: Agencia Nacional de Promoción Científica y Tecnológica, PAE22257, PICT512, PICT38251 
536 |a Detalles de la financiación: Universidad de Buenos Aires 
536 |a Detalles de la financiación: This work was supported by grants of Universidad de Buenos Aires and Agencia Nacional de Promoción Científica y Tecnológica (PAE22257, PICT512 and PICT38251). XRR measurements were performed at LNLS (6060-D12A-XRD1-8693). The authors would like to thank Diego Lamas for XRD studies at CINSO (CITEFA-CONICET), Enrique San Román and Martín Mirenda for transmittance measurements at DQIAQF (FCEN-Universidad de Buenos Aires) and Elena Forlerer for performing the scratch test at CAC-CNEA. 
593 |a Consejo Nacional de Investigaciones Científicas y Técnicas, Buenos Aires, Argentina 
593 |a Instituto de Física del Plasma, Conicet, fcen, Universidad de Buenos Aires, Ciudad Universitaria Pab. I, 1428 Buenos Aires, Argentina 
593 |a Facultad de Ciencias Exactas, Químicas y Naturales, Universidad Nacional de Misiones, Félix de Azara 1552, 3300 Posadas, Misiones, Argentina 
593 |a Gerencia Química, Comisión Nacional de Energía Atómica, Av. Gral. Paz 1499, 1650 San Martín, Prov. de Buenos Aires, Argentina 
593 |a Universidad Nacional de Gral, San Martín, Peatonal Belgrano 3563, 1650 San Martín, Prov. de Buenos Aires, Argentina 
690 1 0 |a CATHODIC ARC DEPOSITION 
690 1 0 |a CR(VI) PHOTOCATALYTIC REDUCTION 
690 1 0 |a HETEROGENEOUS PHOTOCATALYSIS 
690 1 0 |a THIN FILMS 
690 1 0 |a TIO2 
690 1 0 |a ADHESION PROPERTIES 
690 1 0 |a ANATASE TIO 
690 1 0 |a AQUEOUS SYSTEM 
690 1 0 |a CATHODIC ARC 
690 1 0 |a CATHODIC ARC DEPOSITION 
690 1 0 |a COATING THICKNESS 
690 1 0 |a CR REDUCTIONS 
690 1 0 |a DEGUSSA 
690 1 0 |a DIP COATING 
690 1 0 |a GLASS SUBSTRATES 
690 1 0 |a HETEROGENEOUS PHOTOCATALYSIS 
690 1 0 |a KINETIC BEHAVIOR 
690 1 0 |a MASS DENSITIES 
690 1 0 |a NEW MATERIAL 
690 1 0 |a PHOTOACTIVITY 
690 1 0 |a PHOTOCATALYTIC ACTIVITIES 
690 1 0 |a PHOTOCATALYTIC REDUCTION 
690 1 0 |a PHOTOREACTORS 
690 1 0 |a TIO 
690 1 0 |a X-RAY REFLECTOMETRY 
690 1 0 |a CHROMIUM COMPOUNDS 
690 1 0 |a COATINGS 
690 1 0 |a PHOTOCATALYSIS 
690 1 0 |a SUBSTRATES 
690 1 0 |a THICKNESS MEASUREMENT 
690 1 0 |a THIN FILMS 
690 1 0 |a TITANIUM DIOXIDE 
690 1 0 |a VAPOR DEPOSITION 
690 1 0 |a DEPOSITION 
700 1 |a Márquez, Adriana Beatriz 
700 1 |a Vera, M.L. 
700 1 |a Meichtry, J.M. 
700 1 |a Litter, M.I. 
773 0 |d 2011  |g v. 101  |h pp. 676-681  |k n. 3-4  |p Appl. Catal. B Environ.  |x 09263373  |w (AR-BaUEN)CENRE-3757  |t Applied Catalysis B: Environmental 
856 4 1 |u https://www.scopus.com/inward/record.uri?eid=2-s2.0-78650306520&doi=10.1016%2fj.apcatb.2010.11.009&partnerID=40&md5=fc3280080d3df48849a91e79a133576d  |y Registro en Scopus 
856 4 0 |u https://doi.org/10.1016/j.apcatb.2010.11.009  |y DOI 
856 4 0 |u https://hdl.handle.net/20.500.12110/paper_09263373_v101_n3-4_p676_Kleiman  |y Handle 
856 4 0 |u https://bibliotecadigital.exactas.uba.ar/collection/paper/document/paper_09263373_v101_n3-4_p676_Kleiman  |y Registro en la Biblioteca Digital 
961 |a paper_09263373_v101_n3-4_p676_Kleiman  |b paper  |c PE 
962 |a info:eu-repo/semantics/article  |a info:ar-repo/semantics/artículo  |b info:eu-repo/semantics/publishedVersion 
999 |c 71815 

Ejemplares similares