Determination of the Crack Propagation Direction of Fractured Ductile Cast Iron Based on the Characteristic Features of the Surface

In this article, the characteristic fractographic features of ductile cast irons with different metallic matrices were analysed. Several heat treatment cycles were carried out on samples from the same cast iron melt in order to obtain ferritic ductile iron, pearlitic ductile iron and austempered duc...

Descripción completa

Guardado en:

Detalles Bibliográficos
Autores principales:	Fernandino, Diego O., Boeri, Roberto Enrique
Formato:	Other
Lenguaje:	Inglés
Publicado:	INTEMA - UNMdP-CONICET 2014
Materias:	Ductile Iron Fracture Surface Roughness Bending Crack Propagation
Acceso en línea:	http://rinfi.fi.mdp.edu.ar/handle/123456789/57
Aporte de:	RINFI - Facultad de Ingeniería (UNMdP) de Universidad Nacional de Mar del Plata (UNMdP)

Ejemplares similares

High-Temperature Corrosion Fatigue of a Ferritic Ductile Cast Iron in Inert and Corrosive Environments at 700ºC
por: Ekström, M., et al.
Publicado: (2014)

Crack-front propagation during three-point-bending tests of polymethyl-methacrylate beams
por: Loya, J.A., et al.
Publicado: (2010)

Determination of the Crack Propagation Direction of Fractured Ductile Cast Iron Based on the Characteristic Features of the Surface
por: Fernandino, D., et al.
Publicado: (2014)

Environmental Embrittlement of Austempered Ductile Iron (ADI)– A Review
por: Boeri, Roberto Enrique, et al.
Publicado: (2014)

Study of Shrinkage Porosity in Spheroidal Graphite Cast Iron
por: Tenaglia, Nicolás, et al.
Publicado: (2014)

Trace elements and the control limits in ductile iron
por: Magnusson Åberg, L., et al.
Publicado: (2014)

Numerical Simulation of Dimensional Change During Austempering Heat Treatment in Ductile Cast Iron
por: Boccardo, A.D., et al.
Publicado: (2014)

The Occurrence and the Effect of Casting Skin in Compacted Graphite Iron
por: Boonmee, S., et al.
Publicado: (2014)

Criteria for crack extension in cylindrical pressure vessels
por: Hanh, G. T., et al.
Publicado: (1969)

Occurrence and Behavior of Mo-Containing Precipitations in Nodular Cast Iron at High Temperatures
por: Dekker, L., et al.
Publicado: (2014)

Modelling of Density Changes of Nodular Cast Iron During Solidification by Cellular Automaton
por: Gurgul, D., et al.
Publicado: (2014)

Long-term behavior of cracked fiber reinforced concrete under service conditions
por: Monetti, Diego Hernán, et al.
Publicado: (2019)

On Microstructure-Based Mechanical Behaviour of a Ductile Iron Component
por: Svensson, I.L., et al.
Publicado: (2014)

Feeding Against Gravity with Spot Feeders in High Silicon Ductile Iron
por: Vedel-Smith, N.K., et al.
Publicado: (2014)

Electron microscope study of surface markins left by unsteady cleavage crack propagation in NaCl single crystals
por: Wainer, L. S. de, et al.
Publicado: (1978)

Effect of Thermo-mechanical Processing Parameters on Phase Transformation and Hardness of Dual Matrix Ductile Iron
por: Soliman, M., et al.
Publicado: (2014)

Fracture on rubber-metallic cord composites
por: Marzocca, A.J., et al.

Fracture on rubber-metallic cord composites
por: Marzocca, Angel José
Publicado: (1988)

Cracks and fracture /
por: Broberg, K. Bertram
Publicado: (1999)

Cracks as sink of irradiation created point defects
por: Sarce, Alicia
Publicado: (2000)

The effect of the point defects on the behavior of a crack inside of a pressure tube
por: Sarce, Alicia
Publicado: (2001)

Ductile iron handbook
por: Alagarsamy, A.
Publicado: (1993)

A Review of Side-lined Chunky Graphite Phenomena
por: Borgström, H., et al.
Publicado: (2014)

Corrosion Mechanisms in ADI Parts
por: Sosa, A.D., et al.
Publicado: (2014)

Applications of fracture mechanics to reinforced concrete /
Publicado: (2005)

Fractura
por: De Vedia, L. A., et al.
Publicado: (1976)

Numerical experiments of fracture-induced velocity and attenuation anisotropy
por: Carcione, J. M., et al.
Publicado: (2012)

Erratum: "Numerical experiments of fracture-induced velocity and attenuation anisotropy"
por: Carcione, J. M., et al.
Publicado: (2014)

Fluid pressure diffusion effects on the excess compliance matrix of porous rocks containing aligned fractures
por: Castromán, Gabriel Alejandro, et al.
Publicado: (2020)

Precipitate morphologies predicted using discrete lattice descriptions
por: Sarce, Alicia
Publicado: (1996)

Grain boundary sink strength in anisotropic materials
por: Sarce, Alicia, et al.
Publicado: (1990)

The life of cracks : theory and application /
por: Glodez, Srecko, et al.
Publicado: (2020)

Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions
por: Zadorozne, N.S., et al.

Anodic characteristics and stress corrosion cracking behavior of nickel rich alloys in bicarbonate and buffer solutions
por: Carranza, Ricardo Mario
Publicado: (2016)

Transición dúctil-frágil de aceros ferríticos: análisis estadístico de resultados experimentales
por: Larrainzar, César Osvaldo
Publicado: (2010)

Rockwood & Wilkins' fractures in children /
Publicado: (2015)

Distribution of Some Active Elements in Primary Graphite Precipitates
por: Theuwissen, K., et al.
Publicado: (2014)

An oblivious password cracking server
por: Calvo, Aureliano, et al.
Publicado: (2012)

Elastic-plastic fracture : a symposium /
Publicado: (1979)

Contact fatigue behavior of α-Al PROOF 2 O -Ti(C,N) CVD coated WC-Co under dry and wet conditions
por: Sosa, D.A., et al.
Publicado: (2020)