High-Temperature Corrosion Fatigue of a Ferritic Ductile Cast Iron in Inert and Corrosive Environments at 700ºC
In the present work, low-cycle fatigue testing of a ferritic ductile cast iron named SiMo51 has been carried out in three atmospheres: argon, air and a synthetic diesel exhaust-gas at 700C. The fatigue life was reduced up to 80% in the worst case. Two crack growth mechanisms were observed and direc...
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | Other |
| Lenguaje: | Inglés |
| Publicado: |
INTEMA - UNMdP-CONICET
2014
|
| Materias: | |
| Acceso en línea: | http://rinfi.fi.mdp.edu.ar/handle/123456789/19 |
| Aporte de: |
| Sumario: | In the present work, low-cycle fatigue testing of a ferritic ductile cast iron named SiMo51 has been carried out in three atmospheres: argon, air and a synthetic diesel exhaust-gas at 700C. The fatigue life was reduced up to 80% in the worst case. Two crack growth mechanisms were observed and directly linked to oxidation. At weak oxidation, a nodule-to-nodule crack growth occurred. At strong oxidation, crack growth occurred through oxidized material in front of the crack tip. |
|---|