Inhibition of mild steel corrosion in HCl solution using chitosan
The efficiency of chitosan (a naturally occurring polymer) as a corrosion inhibitor for mild steel in 0.1 M HCl was investigated by gravimetric, potentiodynamic polarization, electrochemical impedance spectroscopy measurements, scanning electron microscopy, and UV–visible analysis. The polymer was f...
Guardado en:
| Autores principales: | Umoren, Saviour Alphonsus, Banera, Mauro Jonathan, Alonso García, Teodoro, Gervasi, Claudio Alfredo, Mirífico, María Virginia |
|---|---|
| Formato: | Articulo |
| Lenguaje: | Inglés |
| Publicado: |
2013
|
| Materias: | |
| Acceso en línea: | http://sedici.unlp.edu.ar/handle/10915/137338 |
| Aporte de: |
Ejemplares similares
-
A comparative pitting corrosion study of mild steel in different alkaline solutions containing salts with sulphur-containing anions
por: Vásquez Moll, Victor Dennis, et al.
Publicado: (1984) -
Inhibition of steel corrosion by calcium benzoate adsorption in nitrate solutions
por: Blustein, Guillermo, et al.
Publicado: (2005) -
Amphiphilic amido-amine as an effective corrosion inhibitor for mild steel exposed to CO2 saturated solution: Polarization, EIS and PM-IRRAS studies
por: Desimone, M.P., et al. -
Amphiphilic amido-amine as an effective corrosion inhibitor for mild steel exposed to CO2 saturated solution: Polarization, EIS and PM-IRRAS studies
Publicado: (2011) -
The effect of temperature and concentration on the corrosion inhibition mechanism of an amphiphilic amido-amine in CO2 saturated solution
por: Desimone, M.P., et al.