Influence of the zirconia transformation on the thermal behavior of zircon-zirconia composites
During a heating–cooling cycle, zirconia (ZrO2) undergoes a martensitic transformation from monoclinic to tetragonal structure phases, which presents special hysteresis loop in the dilatometry curve at temperatures between 800 and 1100 °C. Monoclinic zirconia (m-ZrO2) particles reinforced ceramic ma...
Guardado en:
| Autores principales: | Rendtorff Birrer, Nicolás Maximiliano, Suárez, Gustavo, Sakka, Yoshio, Aglietti, Esteban Fausto |
|---|---|
| Formato: | Articulo |
| Lenguaje: | Inglés |
| Publicado: |
2012
|
| Materias: | |
| Acceso en línea: | http://sedici.unlp.edu.ar/handle/10915/131391 |
| Aporte de: |
Ejemplares similares
-
Thermal behavior of Mullite–Zirconia–Zircon composites : Influence of Zirconia phase transformation
por: Rendtorff Birrer, Nicolás Maximiliano, et al.
Publicado: (2011) -
Resistencia a la corrosión por vidrios fundidos de materiales de mullita-zirconia-zircón
por: Rendtorff Birrer, Nicolás Maximiliano, et al.
Publicado: (2009) -
Partially Stabilized Zirconia (3Y-ZrO₂) Aluminum Borate (Al₁₈B₄O₃₃) Needles Composite Materials by Direct Sintering
por: Martínez, Juan Manuel, et al.
Publicado: (2021) -
Zirconia reinforcement of cement free Alumina refractory castables by two routes
por: Rendtorff Birrer, Nicolás Maximiliano, et al.
Publicado: (2012) -
Relation Between Mechanical and Textural Properties of Dense Materials of Tetragonal and Cubic Zirconia
por: Gómez, Sofía, et al.
Publicado: (2016)